0.2 0.3mm C Epoxy Resin Impregnated Mesh Polyester Fiberglass Banding Tape
1. Introduction:
JIANGNAN H200-W,F150-G-W The banding tapes are of high quality, which consist of parallel twisted E-glass yarns preimpregnated with a special thermosetting polyester resin, It consists of parallel twisted E-glass yarns Preimpregnated with a special thermosetting polyester resin, it is pliable and tacky, web structure provides easy unwind without glass trands separation and overlapping.
It's widely used in AC. DC motors, generators and transformers especially in traction motors.
2. Specification
|
Type | (mm)
Thickness | (mm)
Tolerance | (mm)
Width | (mm)
Tolerance |
Put up |
| H200
F150
| 0.20 | ±0.03 | 10 | ±1 |
pancake or spool |
| 15 | ±1.5 |
| 0.30 | ±0.03 |
| 20.25.30.50.60 | ±2 |
3. Curing condition(Time to bring the piece to temperature is not considered)
|
Temperature | ℃ | 160 | 150 | 135 | 120 | 115 |
|
Time |
Hours | 2.5 | 3 | 5 | 14 | 20 |
4. Storage stability
|
Storage temperature | ℃ | 10 | 15 | 20 | 30 |
|
Time | H200 |
Months | 24 | 18 | 12 | 8 |
| F150 | 20 | 15 | 10 | 6 |
5. Properties
|
Item |
Unit |
Figure |
|
Type | — | H200 | F150- |
|
Thermal class | — | H(200℃) | F(155℃) |
|
Volatile content | % | ≤2 |
|
Loss of weight at calcination | % | 26±2 |
|
Soluble resin content | % | ≥90 |
|
Tensile strength before curing | N/cm | 0.20mm | ≥1200 | ≥1000 |
| 0.30mm | ≥2000 | ≥1500 |
|
Maximum pull while banding | N/cm | 0.20mm | ≥600 | ≥500 |
| 0.30mm | ≥1000 | ≥800 |
|
Tensile strength of ringlike sample at room temperature after curing | Mpa | 20℃ |
| ≥1000 | ≥900 |
|
Tensile strength of ringlike sample at working temperature after curing | Mpa | 200℃ | 155℃ |
| ≥700 | ≥560 |
|
Proof tracking index | V | ≥500 |
|
Arc resistance | S | ≥160 |
|
Dielectric strength | KV/mm | ≥12 |
|
Thermosetting | — | OK |
|
Loss of tensile strength after soaked in oil | % | ≤10 |
6. Features:
With proprietary technology and advanced equipment
Reputed for consisting of parallel twisted e-glass yarnspre-impregnated with special thermosetting polyester resin
Widely used in AC/DC motors, generators and transformers
Widths: 10, 15, 20, 25, 30, 50 and 60mm
Thicknesses: 0.17, 0.20, 0.25 and 0.30mm
It has class F and H
7. Application fields:
Rotor banding
Transformer banding
Commuator banding
General purpose
Rotor banding Large-transformer banding Transformer banding